|本期目录/Table of Contents|

[1]DO Khai Ly,钟申洁,徐 浪,等.耐洗型疏水疏油丝绸织物的制备及性能研究[J].丝绸,2020,57(12):121105.
 DO Khai Ly,ZHONG Shenjie,XU Lang,et al.Preparation of hydrophobic and oleophobic silk fabric with good washing durability and research on its performance[J].Journal of Silk,2020,57(12):121105.
点击复制

耐洗型疏水疏油丝绸织物的制备及性能研究(PDF)

《丝绸》[ISSN:1001-7003/CN:33-1122/TS]

卷:
57
期数:
2020年12期
页码:
121105
栏目:
研究与技术
出版日期:
2020-12-20

文章信息/Info

Title:
Preparation of hydrophobic and oleophobic silk fabric with good washing durability and research on its performance
文章编号:
1001-7003(2020)12-0000-00
作者:
DO Khai Ly钟申洁徐 浪左 甜易玲敏
浙江理工大学 a. 纺织科学与工程学院;b. 先进纺织材料与制备技术教育部重点实验室; c.生态染整技术教育部工程研究中心,杭州 310018
Author(s):
DO Khai Ly ZHONG Shenjie XU Lang ZUO Tian YI Lingmin
a. College of Textile Science and Engineering; b. Key Laboratory of Advanced Textile Materials & Manufacturing Technology, Ministry of Education; c. Engineering Research Center for Eco-Dyeing & Finishing of Textiles, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
丝绸织物疏水疏油耐洗牢度疏水改性SiO2
Keywords:
silk fabric hydrophobic oleophobic washing durability hydrophobic modified silica
分类号:
TS195.6
doi:
-
文献标志码:
A
摘要:
目前所制备的疏水疏油丝绸织物大多难以同时满足疏水疏油及耐洗性,或制备过程过于复杂。因此,文章提出在丝绸表面浸涂一层疏水改性的二氧化硅纳米粒子以提供一定的粗糙度,随之将聚(偏氟乙烯-六氟丙烯)溶液喷涂于其上以提供低表面能,两者的协同作用可使丝绸织物具有高度的疏水疏油性和良好的耐洗性能。结果显示,通过这一简单易实施的两步法,制备所得丝绸织物表面的水接触角高达149.5°、滚动角小至5.5°,色拉油的接触角可达132°,表现出高度的疏水疏油性。经20次标准洗涤后,水接触角仍在140°以上,且滚动角小于10°,表现出优异的耐洗色牢度。
Abstract:
It is difficult for current hydrophobic and oleophobic silk fabrics to meet hydrophobic and oleophobic characteristics as well as washing durability at the same time, or the preparation process is too complex. Thus, Therefore, in this study, we proposed to coat hydrophobic modified silica nanoparticles on the fiber surface to provide certain roughness, and then spray poly(vinylidene fluoride-hexafluoropropylene) (PVDF-HFP) to provide low surface energy. The synergistic effect of the two could make the silk fabric have high hydrophobic and oleophobic properties as well as good washing durability . The results indicated that via this simple two-step method, the prepared silk fabric presented a water contact angle (WCA) of 149.5°, a water sliding angle (WSA) of 5.5°, and an oil contact angle (OCA) of 132.0°, demonstrating the high hydrophobicity and oleophobicity of silk. After standard washing for 20 times, the WCA was still more than 140° and the WSA was less than 10°, showing excellent laundering durability.

参考文献/References:

[1] WANG F, PI J, SONG F, et al. A superhydrophobic coating to create multi-functional materials with mechanical/chemical/physical robustness[J]. Chemical Engineering Journal, 2020, 381:122539.
[2] PAN G M, XIAO X Y, YU N L, et al. Fabrication of superhydrophobic coatings on cotton fabric using ultrasound-assisted in-situ growth method[J]. Progress in Organic Coatings, 2018, 125: 463-471.
[3] HE Z C, B AO B W, F AN J, et al. Photochromic cotton fabric based on microcapsule technology with anti-fouling properties[J]. Colloids and Surfaces A : Physicochemical and Engineering Aspects, 2020, 594 :124661.
[4] WU J D, ZHANG C, XU S, et al. Preparation of zwitterionic polymer-functionalized cotton fabrics and the performance of anti-biofouling and long-term biofilm resistance[J]. Colloid and Interface Science Communications, 2018, 24: 98-104.
[5] CHEN K L, ZHOU J L, CHE X G, et al. One-step synthesis of core shell cellulose-silica/n-octadecane microcapsules and their application in waterborne self-healing multiple protective fabric coatings[J]. Journal of Colloid and Interface Science, 2020, 566: 401-410.
[6] KALE B M, WIENER J, MILITKY J, et al. Coating of cellulose-TiO2 nanoparticles on cotton fabric for durable photocatalytic self-cleaning and stiffness[J]. Carbohydrate Polymers, 2016, 150: 107-113.
[7] QIN R H, SONG Y H, NIU M, et al. Construction of flame retardant coating on polyester fabric with ammonium polyphosphate and carbon microspheres[J]. Polymer Degradation and Stability, 2019, 171:109028.
[8] PAN G M, XIAO X Y, YE Z H. Fabrication of stable superhydrophobic coating on fabric with mechanical durability, UV resistance and high oil-water separation efficiency[J]. Surface & Coatings Technology, 2019, 360: 318-328.
[9] OMENETTO F G, KAPLAN D L. New opportunities for an ancient material[J]. Science, 2010, 329: 528-531.
[10] LIU X S, XING T L, XU D M, et al. Study on novel eco-friendly anti-creasing agents for natural silk fabric[J]. Chinese Chemical Lettles, 2012, 23: 665-668.
[11] CHEN F G, LIU X, YANG H Y, et al. A simple one-step approach to fabrication of highly hydrophobic silk fabrics[J]. Applied Surface Science, 2016, 360: 207-212.
[12] HUANG J J, YANG Y Y, YANG L, et al. Fabrication of multifunctional silk fabrics via one step in-situ synthesis of ZnO[J]. Materials Letters, 2019, 237: 149-151.
[13] WANG H, ZHOU H, GESTOS A, et al. Robust, superamphiphobic fabric with multiple self-healing ability against both physical and chemical damages[J]. ACS Applied Materials & Interfaces, 2013, 5: 10221-10226.
[14] ASLANIDOU D, KARAPANAGIOTIS I, PANAYIOTOU C. Superhydrophobic, superoleophobic coatings for the protection of silk textiles[J]. Progress in Organic Coatings, 2016, 97: 44-52.
[15] CHENG Y, ZHUA T X, LI S H, et al. A novel strategy for fabricating robust superhydrophobic fabrics by environmentally-friendly enzyme etching[J]. Chemical Engineering Journal, 2019, 355: 290-298.
[16] CHEN F G, YANG H Y, LIU X, et al. Facile fabrication of multifunctional hybrid silk fabrics with controllable surface wettability and laundering durability[J]. ACS Applied Materials & Interfaces, 2016, 8(8): 5653-5660.
[17] ST?BER W, FINK A, BOHN E. Controlled growth of monodisperse silica spheres in the micron size range[J]. Journal of Colloid and Interface Science, 1968, 26: 62-69.
[18] NITAYAPHAT W, JIRAWONGCHAROEN P, TRIJATURON T. Self-cleaning properties of silk fabrics functionalized with TiO2/SiO2 composites[J]. Journal of Natural Fibers, 2018, 15: 262-272.
[19] PALCHAN I, CRESPON M, ESTRADE-SZWARCKOPF H, et al. Graphite fluorides: an XPS study of a new type of C-F bonding[J]. Chemical Physics Letters, 1989, 157(4): 321-327.
[20] LIANG Z H, ZHOU Z Z, DONG B H, et al. Fabrication of superhydrophobic and UV-resistant silk fabrics with laundering durability and chemical stabilities[J]. Coatings, 2020, 10(4): 349.

备注/Memo

备注/Memo:
基金项目:浙江省基础公益研究计划资助项目(LGG18E030009)
收稿日期:2020-05-24
作者简介:Do Khai Ly (1993—),女,硕士研究生,研究方向为纺织化学与染整工程
通信作者:易玲敏,教授,lmyi@zstu.edu.cn
更新日期/Last Update: 2020-11-13